What are Early Strength Agents?

The spread of the novel coronavirus is taking a direct hit on the operations of airlines in Asia. About 500,000 flights taking off and landing in mainland China have been canceled since January, according to aviation information company Cerium. Tourists and business trips have plummeted. On the booking website, there are a large number of air tickets for local routes with a price reduction of nearly 90% compared with the original price and only tens of yuan for a one-way trip.
In February, China's aviation industry recorded its largest single-month loss of 24.59 billion yuan, of which airlines lost 20.96 billion yuan.
Data from the Civil Aviation Administration of China showed that in February, the number of passengers traveling by air fell 84.5% year-on-year to 8.34 million.
The stagnation of the Asian aviation industry has brought volatility to early strength agent.

What are Early Strength Agents?

Early strength agent is an admixture which accelerates the development of concrete early strength and has no significant effect on later strength. Early strength agent can accelerate the hardening process of concrete under normal temperature and low-temperature load temperature (not less than -5℃), and is used for winter construction and emergency repair projects.

Early Strength Agents Performance

Early strength agent refers to the admixture which can accelerate the development of early strength of concrete. The main mechanism of action is to accelerate the hydration rate of cement, and accelerate the early crystallization and precipitation of hydration products. The main function is to shorten the concrete construction curing period, speed up the construction progress, and improve the template turnover rate. 

Where can Early Strength Agents be Used? 

1. Early strength agent is suitable for steam curing concrete and normal temperature, low temperature and minimum temperature is not less than -5℃ environment construction of early strength requirements of concrete engineering. Early strength agent should not be used in hot environment. 

2.The chemical substances that harm the human body or pollute the environment after mixing concrete shall not be used as early strength agents. Early strength agent containing hexavalent chromium salt, nitrite, and other harmful components is strictly prohibited for drinking water engineering and food contact engineering. Ammonium nitrate shall not be used in office, residential and other construction projects.

Classification of Early Strength Agents 

Early strength agents mainly include inorganic salts (chlorine salts, phosphates) and organic amines, and organic-inorganic compounds.

1. Chloride salts early strength agents

Chlorine salts early strength agent mainly includes calcium chloride, potassium chloride, aluminum chloride and ferric chloride, among which calcium chloride is the most widely used. Calcium chloride is a white powdery substance, and its appropriate dosage is 0.5% ~ 1.0% of the cement quality, which can improve the 3d strength of concrete by 50% ~ 10% and the 7d strength by 20% ~ 40%. Meanwhile, it can reduce the freezing point of water in concrete and prevent concrete from being frozen in the early stage.

Using calcium chloride as early strength agent, the biggest disadvantage of containing Cl- ions, will make steel corrosion, and lead to concrete cracking. In order to inhibit the corrosion effect of calcium chloride on steel bars, calcium chloride and sodium nitrite (NaNO2) are often combined. 

2. Sulfate early strength agents

Sulfate early strength agent, mainly sodium sulfate, calcium thiosulfate, aluminum sulfate, aluminum potassium sulfate, and sodium sulfate is used more. Sodium sulfate is white powdery thing, the general admixture amount is 0.5% ~ 2.0%, when admixture amount is 1% ~ 1.5%, the time that achieves concrete design strength 70% can shorten half or so. 

Sodium sulfate has no corrosion effect on steel bar, and is suitable for concrete which is not allowed to be mixed with chlorine salt. However, due to its action with calcium hydroxide to generate strong alkali NaOH, in order to prevent alkali aggregate reaction, sodium sulfate is strictly prohibited for concrete containing active aggregate, at the same time, attention should be paid to not excessive mixing, so as not to lead to the late expansion of concrete cracking damage, and prevent concrete surface "frost". 

3. Organic amine early strength agents

Organic amine early strength agents mainly include triethanolamine, triisopropanolamine and so on, among which triethanolamine is the best early strength agent. 

Triethanolamine is a colorless or light-yellow oily liquid, alkaline, and soluble in water. The early strength of concrete can be improved by adding 0.02% ~ 0.05% of cement quality.  Triethanolamine has a slight retarding effect on concrete, and too much of it will cause serious retarding and concrete strength to drop, so the dosage should be strictly controlled.

Concrete Additives Supplier

TRUNNANO is a reliable concrete additives supplier with over 12-year experience in nano-building energy conservation and nanotechnology development.

If you are looking for high-quality concrete early strength agents, please feel free to contact us and send an inquiry. (sales@cabr-concrete.com)

We accept payment via Credit Card, T/T, West Union, and Paypal. TRUNNANO will ship the goods to customers overseas through FedEx, DHL, by air, or by sea.

The negative electrode material is the carrier of lithium ions and electrons during the charging process of the battery and plays the role of energy storage and release. In the battery cost, the negative electrode material accounts for about 5%-15%, which is one of the important raw materials for lithium-ion batteries. The global sales of lithium battery anode materials are about 100,000 tons, mainly in China and Japan. According to the current growth trend of new energy vehicles, the demand for anode materials will also show a state of continuous growth. At present, the global lithium battery anode materials are still dominated by natural/artificial graphite, and new anode materials such as mesh carbon microspheres (MCMB), lithium titanate, silicon-based anodes, HC/SC, and metal lithium are also growing rapidly.
Our company provides anode materials and early strength agent. If you need to know more anode materials and early strength agent, please feel free to contact us.

Inquiry us